Plexiglas? Satinice df33 7H
Polymethyl Methacrylate Acrylic
PLEXIGLAS? Satinice df33 7H, based on PLEXIGLAS? 7H, is characterized by diffuse scattering of light.
Typical properties of impact modified PLEXIGLAS? molding compound are
Extruded parts from PLEXIGLAS? Satinice df33 7H are characterized by the following special properties:
Application:
Used for (Co-) extruding profiles and sheets for the construction, furniture and automotive industry.
Examples:
applications that call for light diffusion combined with optimum transmission and velvet matt surface appearance is desired.
Additive | |
Features | |
Uses | - Automotive Applications，Construction Applications，Furniture，Lighting Diffusers，Profiles，Sheet
|
Appearance | |
Forms | |
Processing Method | |
Density | 1.18 | g/cm3 | ISO 1183 |
Melt Volume-Flow Rate (MVR) (230°C/3.8 kg) | 0.0549 | in3/10min | ISO 1133 |
Tensile Modulus | 479000 | psi | ISO 527-2/1 |
Tensile Stress (Break) | 9430 | psi | ISO 527-2/5 |
Tensile Strain (Break) | 4.0 | % | ISO 527-2/5 |
Charpy Unnotched Impact Strength (73°F) | 8.1 | ft·lb/in2 | ISO 179/1eU |
Heat Deflection Temperature |
|
|
|
66 psi, Unannealed | 214 | °F | ISO 75-2/B |
264 psi, Unannealed | 210 | °F | ISO 75-2/A |
Vicat Softening Temperature | 216 | °F | ISO 306/B50 |
CLTE - Flow (32 to 122°F) | 3.7E-5 | in/in/°F | ISO 11359-2 |
Glow Wire Ignition Temperature | 1290 | °F | IEC 60695-2-13 |
Gloss 2 |
|
| ISO 2813 |
105° | 16 |
|
|
90° | 9 |
|
|
Transmittance 3 | 69.0 | % | ISO 13468-2 |
Half-Value Angle | 34.0 | ° | DIN 5036 |
Scattering Power | 0.470 |
| DIN 5036 |
Drying Temperature | < 194 | °F |
|
Drying Time | 2.0 to 3.0 | hr |
|
Melt Temperature | 446 to 500 | °F |
|
Die Temperature | 446 to 500 | °F |
|