Crastin? HR5330HF NC010

Manufacturer: Celanese
Produced At: Import/ China
Product Category: PBT
Product No: CCrastin? HR5330HF NC010
Product Quantity: 25KG / BAG
Product Features: Hydrolysis Resistant

Product information

Crastin? HR5330HF NC010

THERMOPLASTIC POLYESTER RESIN

Product Description:

30% Glass Reinforced, Hydrolysis Resistant, Polybutylene Terephthalate

Filler / Reinforcement	Glass Fiber, 30% Filler by Weight
Additive	Mold Release
Features	Hydrolysis Resistant
RoHS Compliance	Contact Manufacturer
Forms	Pellets
Processing Method	Injection Molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Shear Modulus vs. Temperature, Dynamic (ISO 11403-1) Shear Stress vs. Shear Rate (ISO 11403-1) Specific Volume vs Temperature (ISO 11403-2) Tensile Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)
Part Marking Code (ISO 11469)	PBT-IGF30
Resin ID (ISO 1043)	PBT-IGF30

Physical	Nominal Value	Unit	Test Method
Density	1.50	g/cm3	ISO 1183
Melt Volume-Flow Rate (MVR) (250°C/2.16 kg)	0.519	in3/10min	ISO 1133
Molding Shrinkage			ISO 294-4
Across Flow	1.0	%
Flow	0.30	%
Water Absorption			ISO 62
Saturation, 73°F, 0.0787 in	0.35	%
Equilibrium, 73°F, 0.0787 in, 50% RH	0.15	%
Viscosity Number	95.0	cm3/g	ISO 307
Flow Length 3 (78.7 mil)	14	in

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1.23E+6	psi	ISO 527-2
Tensile Stress (Break)	18100	psi	ISO 527-2
Tensile Strain (Break)	3.2	%	ISO 527-2
Flexural Modulus	1.09E+6	psi	ISO 178
Flexural Stress	29000	psi	ISO 178
Poisson's Ratio 4	0.34		ISO 527
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-22°F	5.5	ft·lb/in2
73°F	6.2	ft·lb/in2
Charpy Unnotched Impact Strength (73°F)	33	ft·lb/in2	ISO 179/1eU
Notched Izod Impact Strength			ISO 180/1A
-40°F	5.2	ft·lb/in2
73°F	6.7	ft·lb/in2
Unnotched Izod Impact Strength (73°F)	31	ft·lb/in2	ISO 180/1U

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
66 psi, Unannealed	430	°F	ISO 75-2/B
264 psi, Unannealed	405	°F	ISO 75-2/A
Glass Transition Temperature 5	149	°F	ISO 11357-2
Vicat Softening Temperature	419	°F	ISO 306/B50
Melting Temperature 5	437	°F	ISO 11357-3
CLTE			ISO 11359-2
Flow	1.1E-5	in/in/°F
Flow : -40 to 73°F	1.4E-5	in/in/°F
Flow : 131 to 320°F	8.3E-6	in/in/°F
Transverse	8.3E-5	in/in/°F
Transverse : -40 to 73°F	5.0E-5	in/in/°F
Transverse : 131 to 320°F	8.1E-5	in/in/°F

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+13	ohms	IEC 60093
Volume Resistivity	> 1.0E+15	ohms·cm	IEC 60093
Electric Strength			IEC 60243-1
--	1100	V/mil
0.0394 in 6	790	V/mil
Relative Permittivity			IEC 60250
100 Hz	4.40
1 MHz	4.10
Dissipation Factor			IEC 60250
100 Hz	2.5E-3
1 MHz	0.020
Comparative Tracking Index	450	V	IEC 60112
Flammability	Nominal Value	Unit	Test Method
Burning Rate 7 (0.0394 in)	1.2	in/min	ISO 3795
Flame Rating
0.030 in	HB		UL 94, IEC 60695-11-10, -20
0.06 in	HB		IEC 60695-11-10, -20
Oxygen Index	19	%	ISO 4589-2
FMVSS Flammability	B		FMVSS 302

Fill Analysis	Nominal Value	Unit
Melt Density	1.29	g/cm3
Ejection Temperature	338	°F
Specific Heat Capacity of Melt	0.413	Btu/lb/°F
Thermal Conductivity of Melt	1.9	Btu·in/hr/ft2/°F

Injection	Nominal Value	Unit
Drying Temperature	248	°F
Drying Time - Desiccant Dryer	2.0 to 4.0	hr
Suggested Max Moisture	0.040	%
Processing (Melt) Temp	464 to 500	°F
Melt Temperature, Optimum	482	°F
Mold Temperature	86 to 266	°F
Mold Temperature, Optimum	176	°F
Holding Pressure	8700	psi
Back Pressure	As low as possible
Drying Recommended	yes
Hold Pressure Time	3.00	s/mm

Products

Products

Crastin? HR5330HF NC010