Manufacturer: Celanese
Produced At: Import/ China
Product Category: PET
Product No: Rynite? 530 NC010
Product Quantity: 25KG / BAG

Rynite? 530 NC010

THERMOPLASTIC POLYESTER RESIN

Product Description:

30% Glass Reinforced Polyethylene Terephthalate

Filler / Reinforcement	Glass Fiber, 30% Filler by Weight
Additive	Mold Release
RoHS Compliance	Contact Manufacturer
Forms	Pellets
Processing Method	Injection Molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Shear Modulus vs. Temperature, Dynamic (ISO 11403-1) Shear Stress vs. Shear Rate (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)
Part Marking Code (ISO 11469)	PET-GF30
Resin ID (ISO 1043)	PET-GF30

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1.60E+6	psi	ISO 527-2
Tensile Stress (Break)	22900	psi	ISO 527-2
Tensile Strain (Break)	2.5	%	ISO 527-2
Tensile Creep Modulus			ISO 899-1
1 hr	1.57E+6	psi
1000 hr	1.28E+6	psi
Flexural Modulus	1.30E+6	psi	ISO 178
Flexural Stress	33400	psi	ISO 178
Poisson's Ratio	0.34		ISO 527
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-40°F	4.8	ft·lb/in2
-22°F	5.2	ft·lb/in2
73°F	5.2	ft·lb/in2
Charpy Unnotched Impact Strength			ISO 179/1eU
-22°F	21	ft·lb/in2
73°F	29	ft·lb/in2

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
66 psi, Unannealed	473	°F	ISO 75-2/B
264 psi, Unannealed	435	°F	ISO 75-2/A
Vicat Softening Temperature	446	°F	ISO 306/B50
Melting Temperature 3	486	°F	ISO 11357-3
CLTE			ISO 11359-2
Flow	5.6E-6	in/in/°F
Flow : -40 to 73°F	1.2E-5	in/in/°F
Flow : 131 to 320°F	2.2E-6	in/in/°F
Transverse	4.5E-5	in/in/°F
Transverse : -40 to 73°F	3.7E-5	in/in/°F
Transverse : 131 to 320°F	5.9E-5	in/in/°F
Thermal Conductivity	2.0	Btu·in/hr/ft2/°F
Effective Thermal Diffusivity	1.30E-7	m2/s

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+14	ohms	IEC 60093
Volume Resistivity	1.0E+15	ohms·cm	IEC 60093
Electric Strength	810	V/mil	IEC 60243-1
Relative Permittivity			IEC 60250
100 Hz	4.20
1 MHz	3.80
Dissipation Factor			IEC 60250
100 Hz	0.013
1 MHz	7.0E-3
Comparative Tracking Index (CTI)	PLC 2		UL 746
Comparative Tracking Index	250	V	IEC 60112
Flammability	Nominal Value	Unit	Test Method
Burning Rate 4 (0.0394 in)	1.5	in/min	ISO 3795
Flame Rating			UL 94, IEC 60695-11-10, -20
0.030 in	HB
0.06 in	HB
Oxygen Index	20	%	ISO 4589-2
FMVSS Flammability	B		FMVSS 302
Fogging - G-value (condensate)	0.0	g	ISO 6452

Fill Analysis	Nominal Value	Unit	Test Method
Ejection Temperature	338	°F
Additional Information	Nominal Value	Unit	Test Method
Emission of Organic Compounds	16.0	μgC/g	VDA 277
Odor	3.00		VDA 270

Injection	Nominal Value	Unit
Drying Temperature	248	°F
Drying Time - Desiccant Dryer	4.0 to 6.0	hr
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	536 to 572	°F
Melt Temperature, Optimum	545	°F
Mold Temperature	248 to 284	°F
Mold Temperature, Optimum	266	°F
Holding Pressure	11600	psi
Back Pressure	As low as possible
Drying Recommended	yes
Hold Pressure Time	4.00	s/mm
Maximum Screw Tangential Speed	472	in/min