VESTAMID? Care ML67
Polyamide 12
VESTAMID?Care ML grades cover a range of polyamide 12 resins of different viscosity for processing via extrusion or injection molding. The VESTAMID?Care ML product range consists of unstabilized base resins as well as stabilized or reinforced compounds.
VESTAMID? Care ML resins are characterized by several outstanding properties, such as high impact & notched impact resistance, dimensional stability, good sliding properties, high abrasion resistance and resistance against chemicals.
Unfilled VESTAMID? Care ML grades are for example the materials of choice for catheters and tubings, where VESTAMID? Care ML materials meet even highest challenges in applications such as angioplasty balloon catheters.
Typical areas of application for reinforced VESTAMID? Care ML grades include housing-parts, monitoring and imaging devices and durable medical equipment. Due to their low water uptake, filled VESTAMID? Care ML grades even resist steam autoclaving for more than 500 cycles. The advantages at a glance :
Features | - Abrasion Resistant，Biocompatible，Chemical Resistant，Good Colorability，Good Processability，High Dimensional Stability，High Impact Resistance，High Toughness，Low Friction
|
Uses | - Medical Devices，Medical/Healthcare Applications，Tubing
|
Agency Ratings | - ISO 10993，USP 88，USP Class VI
|
Processing Method | - Extrusion，Injection Molding
|
Density (73°F) | 1.01 | g/cm3 | ISO 1183 |
Molding Shrinkage |
|
| ISO 294-4 |
Across Flow : 0.0787 in | 1.1 | % |
|
Flow : 0.0787 in | 0.90 | % |
|
Water Absorption |
|
| ISO 62 |
Saturation, 73°F | 1.4 | % |
|
Equilibrium, 73°F, 50% RH | 0.70 | % |
|
Tensile Modulus | 203000 | psi | ISO 527-2 |
Tensile Stress (Yield, 73°F) | 6670 | psi | ISO 527-2 |
Tensile Strain (Yield, 73°F) | 6.0 | % | ISO 527-2 |
Nominal Tensile Strain at Break (73°F) | > 50 | % | ISO 527-2 |
Charpy Notched Impact Strength |
|
| ISO 179/1eA |
-22°F, Complete Break | 2.4 | ft·lb/in2 |
|
73°F, Complete Break | 1.9 | ft·lb/in2 |
|
Charpy Unnotched Impact Strength |
|
| ISO 179/1eU |
-22°F | No Break |
|
|
73°F | No Break |
|
|
Heat Deflection Temperature |
|
|
|
66 psi, Unannealed | 248 | °F | ISO 75-2/B |
264 psi, Unannealed | 122 | °F | ISO 75-2/A |
Vicat Softening Temperature |
|
|
|
-- | 338 | °F | ISO 306/A |
-- | 284 | °F | ISO 306/B |
Melting Temperature (DSC) 2 | 352 | °F | ISO 11357 |
CLTE - Flow (73 to 131°F) | 8.3E-5 | in/in/°F | ISO 11359-2 |
Flammability Classification |
|
| IEC 60695-11-10, -20 |
0.06 in | HB |
|
|
0.13 in | HB |
|
|