VESTAMID? HTplus M3033
Polyphthalamide
Polyphthalamide based on PA10T
VESTAMID HTplus M3033 is a PA 10T-based, black colored, glass-fiber reinforced (30%), heat-stabilized copolyamide. PA 10T is a poly-condensation product of 1,10-decamethylene diamine (10) and terephthalic acid (T). As 1,10-decamethylene diamine is derived from castor oil plants, VESTAMID HTplus M3033 is partially natural resourced and thus bio-based.
Compared to PA 6T-based resins VESTAMID HTplus M3033 has a broader processing window as well as a reduced tendency to absorb water. Therefore the material exhibits less variation in mechanical properties and dimensional changes with humidity.
This resin is especially suited for manufacturing parts subjected to high temperature.
Filler / Reinforcement | |
Additive | |
Features | - Copolymer，Heat Stabilized，High Heat Resistance，Renewable Resource Content
|
Uses | |
Appearance | |
Forms | |
Density (73°F) | 1.36 | g/cm3 | ISO 1183 |
Tensile Modulus | 1.36E+6 | psi | ISO 527-2 |
Tensile Stress (Break) | 24500 | psi | ISO 527-2 |
Tensile Strain (Break) | 2.4 | % | ISO 527-2 |
Charpy Notched Impact Strength |
|
| ISO 179/1eA |
-40°F, Complete Break | 3.6 | ft·lb/in2 |
|
73°F, Complete Break | 4.1 | ft·lb/in2 |
|
Charpy Unnotched Impact Strength |
|
| ISO 179/1eU |
-40°F, Complete Break | 25 | ft·lb/in2 |
|
73°F, Complete Break | 27 | ft·lb/in2 |
|
Heat Deflection Temperature |
|
|
|
66 psi, Unannealed | 543 | °F | ISO 75-2/B |
264 psi, Unannealed | 505 | °F | ISO 75-2/A |
Melting Temperature 2 | 545 | °F | ISO 11357-3 |
Drying Temperature | 248 | °F |
|
Drying Time | > 4.0 | hr |
|