Zytel? HTN 53G50LWSF BK702A
HIGH PERFORMANCE POLYAMIDE RESIN
Product Description:
50% Glass Reinforced High Performance Polyamide with Low Warpage and High Stiffness
Filler / Reinforcement | |
Additive | |
Features | |
RoHS Compliance | |
Forms | |
Processing Method | |
Density | 1.58 | -- | g/cm3 | ISO 1183 |
Molding Shrinkage |
|
|
| ISO 294-4 |
Across Flow | 0.30 | -- | % |
|
Flow | 0.10 | -- | % |
|
Tensile Modulus | 2.47E+6 | 2.32E+6 | psi | ISO 527-2 |
Tensile Stress (Break) | 39200 | 30500 | psi | ISO 527-2 |
Tensile Strain (Break) | 2.4 | 2.6 | % | ISO 527-2 |
Tensile Creep Modulus |
|
|
| ISO 899-1 |
1 hr | -- | 1.60E+6 | psi |
|
1000 hr | -- | 1.16E+6 | psi |
|
Poisson's Ratio | 0.33 | 0.33 |
| ISO 527 |
Charpy Notched Impact Strength |
|
|
| ISO 179/1eA |
-22°F | 6.7 | 7.6 | ft·lb/in2 |
|
73°F | 7.1 | 7.6 | ft·lb/in2 |
|
Charpy Unnotched Impact Strength |
|
|
| ISO 179/1eU |
-22°F | 43 | 43 | ft·lb/in2 |
|
73°F | 43 | 43 | ft·lb/in2 |
|
Heat Deflection Temperature |
|
|
|
|
66 psi, Unannealed | 491 | -- | °F | ISO 75-2/B |
264 psi, Unannealed | 482 | -- | °F | ISO 75-2/A |
Melting Temperature 3 | 500 | -- | °F | ISO 11357-3 |
CLTE |
|
|
| ISO 11359-2 |
Flow | 1.1E-5 | -- | in/in/°F |
|
Transverse | 3.3E-5 | -- | in/in/°F |
|
Surface Resistivity | -- | > 1.0E+15 | ohms | IEC 60093 |
Volume Resistivity | > 1.0E+15 | -- | ohms·cm | IEC 60093 |
Comparative Tracking Index | 550 | -- | V | IEC 60112 |
Burning Rate 4 (0.0394 in) | < 3.9 | -- | in/min | ISO 3795 |
Flame Rating (0.030 in) | HB | -- |
| UL 94, IEC 60695-11-10, -20 |
FMVSS Flammability | B | -- |
| FMVSS 302 |
Drying Temperature | 212 | °F |
|
Drying Time - Desiccant Dryer | 6.0 to 8.0 | hr |
|
Suggested Max Moisture | 0.10 | % |
|
Processing (Melt) Temp | 536 to 572 | °F |
|
Melt Temperature, Optimum | 554 | °F |
|
Mold Temperature | 194 to 230 | °F |
|
Drying Recommended | yes |
|
|